Rapid pressure-less and spark plasma sintering of (Ba 0.85 Ca 0.15 Zr 0.1 T 0.9 )O 3 lead-free piezoelectric ceramics

Home - Blog Detail

by: Vijay Bijalwan, Vladimír Prajzler, Jiří Erhart, Hua Tan, Pavla Roupcová, Dinara Sobola, Pavel Tofel and Karel Maca

Abstract: This work shows for the first time the possibility to sinter BCZT powder compacts by rapid heating rates within one hour of sintering, while achieving good piezoelectric properties. The sintering was performed by rapid (heating rates 100 and 200 • C/min) pressure-less sintering (PLS) at 1550 • C/5-60 min and by SPS sintering (100 • C/min, 1450 • C/5− 60 min and 1500 • C/15− 45 min). The rapid PLS samples reached a relative density up to 94 % and grain sizes of 17-36 μm acquiring d 33 up to 414 pC/N. Although the SPS samples reached full density at 1450 • C, their piezoelectric properties worsened due to smaller grains (10− 15 μm) as well as formation of cracks at dwell times > 30 min. At elevated SPS temperature of 1500 • C/30 min, the d 33 increased to 360 pC/N sustaining full density. Even higher increase in d 33 (424 pC/N) of SPS samples was achieved by post-rapid PLS at 1550 • C/60 min resulting from further expansion in grain size.

https://doi.org/10.1016/j.jeurceramsoc.2020.11.029

Link : [frontend_admin field=64997b393c1b1 edit=false]

The European hub of Piezo Electricity

© 2023 Created by ALLOUARD Bastien, SOUSA BESSA Fabricio, BAVENCOFFE Maxime